| dc.description.abstract | In this work, poly(allylamine hydrochloride) (PAIAm) was modified over its amine group with different equivalents of cyanamide (1:1.2, 1:1.8, 1:2.6, 1:5.2), and poly(allylguanidine hydrochloride) (PAIG) was obtained at different percent conversions. N% values were obtained by elemental analysis and conversion ratio calculated as 45, 71, 98 and 121% for the compounds PAlG1, PAlG2, PAlG3, PAlG4, respectively. Synthesized compounds were also characterized by using FT-IR, FT-Raman, 1H NMR and 13C NMR techniques. Results show that PAIAm was converted to PAIG. Bands at 1760 and 1705 cm-1 in FT-IR and FT-Raman spectra belongs to –C(NH)2+Cl- and C=N bonds and the band at 1150 cm-1 in the FT-IR spectrum belongs to C-N-C bond. Peaks due to guanidine carbons were observed at 160 ppm. According to MIC results, 4, 16, 32, 1024, 1024 μg mL measurements on S. Aureus were recorded for PAlAm, PAlG1, PAlG2, PAlG3 and PAlG4, respectively. | tr_TR |
| dc.language.iso | tur | tr_TR |
| dc.publisher | Fen Bilimleri Enstitüsü | tr_TR |
| dc.subject | Antimicrobial polymers | tr_TR |
| dc.title | Poli(Allil Guanidin.Hcl)'Ün Sentezi, Karakterizasyonu ve Antimikrobiyal Özelliğinin İncelenmesi | tr_TR |
| dc.type | info:eu-repo/semantics/masterThesis | tr_TR |
| dc.callno | 2013/676 | tr_TR |
| dc.contributor.departmentold | Kimya | tr_TR |
| dc.description.ozet | Bu çalışmada poli(allilamin hidroklorür) (PAlAm), farklı oranlarda (1:1,2, 1:1,8, 1:2,6, 1:5,2) siyanamit ile amin grubu üzerinden modifiye edilerek farklı dönüşüm yüzdelerine sahip poli(allilguanidin hidroklorür) (PAlG) elde edilmiştir. Elementel analiz ile belirlenen %N değerleri üzerinden dönüşüm oranları %45, 71, 98 ve 121 olarak hesaplanmıştır. PAlAm ün PAlG e dönüşümü gösterilmiştir. FT-IR ve FT-Raman analizlerinde 1760, 1705 cm-1 de sırasıyla gözlenen –C(NH)2+Cl-, C=N, bağlarına ait bantlar ve PAlG yapılarına ait FT-IR spektrumlarında 1150 cm-1 de gözlenen C-N-C bağına ait bant yapının guanidinleştirildiğini göstermektedir.13C-NMR spektrumlarında guanidin karbonundan kaynaklanan pik 160 ppm civarında gözlenmiştir.Staphylococcus aureusa karşı PAlAm, PAlG1, PAlG2, PAlG3 ve PAlG4 için alınan sonuçlar sırasıyla 4, 16, 32, 1024, 1024 μg mL. | tr_TR |