This thesis aims to examine the joining of steel sheets with a yield strength of up to 1500MPa and aluminum materials by using resistance spot welding (RSW). Effect of electrode geometry and its combinations on the quality of the joint is investigated. Materials used are steel MS1500 and aluminum EN AW-6061-T6. Samples were produced, and iterations were observed on these samples to achieve the optimum combination in terms of mechanical strength by changing parameters such as current, time, and electrode type. The study was carried out on a scale between 11-14kA as current. The force was kept constant in all samples by taking 3kN. Welding times of 10 and 20 cycles were tested. Microstructure analysis, macrostructure analysis, and tensile-shear testing methods were applied to observe the results and achieve the goal of maximizing mechanical strength.. The macrostructure analysis examined the nugget diameter, melted zone geometry, joint geometry, and fracture type. Failure types were determined due to the tensile-shear test. Vickers hardness test was applied to specify the hardness of the joint.
This thesis aims to examine the joining of steel sheets with a yield strength of up to 1500MPa and aluminum materials by using resistance spot welding (RSW). Effect of electrode geometry and its combinations on the quality of the joint is investigated. Materials used are steel MS1500 and aluminum EN AW-6061-T6. Samples were produced, and iterations were observed on these samples to achieve the optimum combination in terms of mechanical strength by changing parameters such as current, time, and electrode type. The study was carried out on a scale between 11-14kA as current. The force was kept constant in all samples by taking 3kN. Welding times of 10 and 20 cycles were tested. Microstructure analysis, macrostructure analysis, and tensile-shear testing methods were applied to observe the results and achieve the goal of maximizing mechanical strength.. The macrostructure analysis examined the nugget diameter, melted zone geometry, joint geometry, and fracture type. Failure types were determined due to the tensile-shear test. Vickers hardness test was applied to specify the hardness of the joint.
Künye
[1] H. M. Mallaradhya, V. Kumar M, R. Ranganatha, S. Darshan, and Lochan, “Resistance Spot Welding, A Review,” Int. J. Mech. Prod. Eng. Res. Dev., vol. 8, pp. 403–418, Apr. 2018, doi: 10.24247/ijmperdapr201846.
[2] P. Podržaj, I. Polajnar, J. Diaci, and Z. Kariž, “Overview of resistance spot welding control,” https://doi.org/10.1179/174329308X283893, vol. 13, no. 3, pp. 215–224, May 2013, doi: 10.1179/174329308X283893.
[3] H. Zhang and J. Senkara, Resistance welding: Fundamentals and applications, second edition. 2011.
[4] S. Shafee, B. B. Naik, and K. Sammaiah, “Resistance Spot Weld Quality Characteristics Improvement By Taguchi Method,” Mater. Today Proc., vol. 2, no. 4–5, pp. 2595–2604, 2015, doi: 10.1016/J.MATPR.2015.07.215.
[5] L. H. Shah and M. Ishak, “Review of Research Progress on Aluminum–Steel Dissimilar Welding,” http://dx.doi.org/10.1080/10426914.2014.880461, vol. 29, no. 8, pp. 928–933, Aug. 2014, doi: 10.1080/10426914.2014.880461.
[6] M. P. Mubiayi and E. Akinlabi, “Friction Stir Welding of Dissimilar Materials between Aluminium Alloys and Copper - An Overview,” undefined, 2013.
[7] K. Martinsen, S. J. Hu, and B. E. Carlson, “Joining of dissimilar materials,” CIRP Ann., vol. 64, no. 2, pp. 679–699, Jan. 2015, doi: 10.1016/J.CIRP.2015.05.006.
[8] M. Pouranvari, “Critical assessment 27: dissimilar resistance spot welding of aluminium/steel: challenges and opportunities,” https://doi.org/10.1080/02670836.2017.1334310, vol. 33, no. 15, pp. 1705–1712, Oct. 2017, doi: 10.1080/02670836.2017.1334310.
[9] K. Miyamoto, S. Nakagawa, C. Sugi, H. Sakurai, and A. Hirose, “Dissimilar joining of aluminum alloy and steel by resistance spot welding,” SAE Tech. Pap., pp. 58–67, 2009, doi: 10.4271/2009-01-0034.
[10] N. Chen, H. P. Wang, B. E. Carlson, D. R. Sigler, and M. Wang, “Fracture mechanisms of Al/steel resistance spot welds in lap shear test,” J. Mater. Process. Technol., vol. 243, pp. 347–354, May 2017, doi: 10.1016/J.JMATPROTEC.2016.12.015.
[11] R. Qiu, C. Iwamoto, and S. Satonaka, “Interfacial microstructure and strength of steel/aluminum alloy joints welded by resistance spot welding with cover plate,” J. Mater. Process. Technol., vol. 209, no. 8, pp. 4186–4193, Apr. 2009, doi: 10.1016/J.JMATPROTEC.2008.11.003.
[12] J. Chen, X. Yuan, Z. Hu, C. Sun, Y. Zhang, and Y. Zhang, “Microstructure and mechanical properties of resistance-spot-welded joints for A5052 aluminum alloy and DP 600 steel,” Mater. Charact., vol. 120, pp. 45–52, Oct. 2016, doi: 10.1016/J.MATCHAR.2016.08.015.
[13] Y. C.-S. and technology of welding and joining and undefined 2003, “Failure mode of spot welds: interfacial versus pullout,” me.sc.edu, Accessed: Oct. 29, 2022. [Online]. Available: http://www.me.sc.edu/fs/pdf/stwj paper published.pdf.
[14] Y. Lu, E. Mayton, H. Song, M. Kimchi, and W. Zhang, “Dissimilar metal joining of aluminum to steel by ultrasonic plus resistance spot welding - Microstructure and mechanical properties,” Mater. Des., vol. 165, p. 107585, Mar. 2019, doi: 10.1016/J.MATDES.2019.107585.
[15] Y.-L. Lee, M. E. Barkey, and H.-T. Kang, “Metal fatigue analysis handbook : practical problem-solving techniques for computer-aided engineering,” 2011.
[16] H. M. Rao, J. Kang, L. Shi, D. R. Sigler, and B. E. Carlson, “Effect of specimen configuration on fatigue properties of dissimilar aluminum to steel resistance spot welds,” undefined, vol. 116, pp. 13–21, Nov. 2018, doi: 10.1016/J.IJFATIGUE.2018.06.009.
[17] J. Kang, Y. Chen, D. Sigler, B. Carlson, and D. S. Wilkinson, “Fatigue Behavior of Dissimilar Aluminum Alloy Spot Welds,” Procedia Eng., vol. 114, pp. 149–156, 2015, doi: 10.1016/J.PROENG.2015.08.053.