Poliüretan Tabanlı Kemik Yapıştırıcısı Formülasyonları
Özet
Millions of people are in need of bone injury treatment for many reasons such as traffic accidents, daily injuries, sports injuries. For the stabilization of bone fractures in the health field; plastering, external stabilization, the use of plates and screws. However, these methods are not suitable for all types of bone fractures. Hard tissue adhesives are needed when the fractures are on an irregular surface, in thin bones or in broken bones proximity to sensitive tissues. For this purpose, it is planned to develop polyurethane based bone adhesive to adhere bone tissues to each other and composite tissue scaffolds consisting of polyurethane and ceramic to support bone tissue formation in damaged area. In this way, it is aimed to develop osteoconductive and osteoinductive bone adhesives and graft formulations which can be shaped according to the shape of the defect area. For this purpose, in the first step of the thesis, polyurethane bone adhesive and tissue scaffold including different size (0,5-1 mm, 1-2 mm and 2-4 mm) and different percentages (20%, 30% and 40% by weight) beta-tricalcium phosphate were prepared. In the second step of the thesis, Fourier Transform Infrared Spectroscopy (FTIR) and Hydrogen-Nuclear Magnetic Resonance (1H-NMR) analyzes were performed to determine the functional groups present in the tissue scaffold and the synthesis of the desired polyurethane structure was verified. The thermal behavior of the material is characterized by differential scanning calorimetry (DSC) analysis. By using scanning electron microscopy (SEM) and micro-computerized tomography (μ-CT), it is observed that the tissue scaffolds have porosity above 90%, the organic and inorganic phases are well integrated with each other and the homogeneous distribution of β-TCP particles in the structure. It was also found that average pore size of the groups are about 267 ± 25 μm.
In the compression tests, performed to determine the mechanical strength of the tissue scaffold candidates, the highest compressive strength was found in the group including 1-2 mm particle size with 40% β-TCP. Also it has been observed that increasing the TCP ratio increases the compression strength.
In order to determine the adhesion strength of the polyurethane based bone adhesive, the fractured bovine rib bones were glued and subjected to mechanical tensile test, and the adhesive strength of the material was determined to be 1,34 MPa.
In the final stage of the thesis, in order to investigate in vitro performance of the polyurethane/β-TCP scaffolds, MG63 human osteosarcoma cells were seeded onto polyurethane/β-TCP tissue scaffolds. To investigate the cell viability and the proliferation Alamar Blue assay was performed. Among the groups, the highest cell viability values were observed in the group containing 40% (w/w) β-TCP with 1-2 mm particle size and this group was found to be more successful than the other groups due to supporting cell proliferation. Cytotoxicity analysis performed by means of the elution method according to ISO 10993-2 showed 85.75% cell viability. This result indicates that the materials are not toxic.
Bağlantı
http://hdl.handle.net/11655/4875Koleksiyonlar
İlgili öğeler
Başlık, yazar, küratör ve konuya göre gösterilen ilgili öğeler.
-
Kemik İliği Yağ Tabakasından Elde Edilen Mezenkimal Kök Hücrelerin Karakterizasyonu ve Subkutan Yağ ve Kemik İliği Kökenli Mezenkimal Kök Hücreleri ile Karşılaştırılması
Tonyalı, Gülsena (Sağlık Bilimleri Enstitüsü, 2020-09)Bone marrow adipose tissue (BMAT) has different properties than other adipose tissues. Recent studies have shown the effects of bone marrow adipose tissue on development / progression of acute myeloblastic leukemia (AML), ... -
İmplant Uygulanacak Alanın Kemik Densitesindeki Farklılıkların İmplant Çevresindeki Marjinal Kemik Seviyelerindeki Değişikliklere Etkisinin İki Farklı İmplant Tipinde İncelenmesi.
Tuğay, Barış (Sağlık Bilimleri Enstitüsü, 2021)Investigation of the effect of differences in bone density on the implant site to the changes in marginal bone levels around the implant in two different implant types. -
FRONTO-ORBİTAL İLERLETME SEGMENTİNE NON-VASKÜLERİZE KEMİK GREFTİ OLARAK DİSTRAKSİYON OSTEOGENEZİ UYGULANAN KRANİOSİNOSTOZ HASTALARININ GEÇ DÖNEM KEMİK KALİTESİNİN MORFOLOJİK, RADYOGRAFİK VE DANSİTOMETRİK YÖNTEMLERLE DEĞERLENDİRİLMESİ
Kaplan, Güven Ozan (Tıp Fakültesi, 2023)Craniosynostosis can be defined as an early fusion of one or more cranial sutures, which results in abnormal cranial shape and restricted skull growth. In treatment, conventional fronto-orbital advancement has remained ...