dc.contributor.authorKurt, Irem
dc.contributor.authorCehreli, Zafer Cavit
dc.contributor.authorOzcirpici, Ayca Arman
dc.contributor.authorSar, Cagla
dc.date.accessioned2021-06-03T08:09:01Z
dc.date.available2021-06-03T08:09:01Z
dc.date.issued2019
dc.identifier.issn0003-3219
dc.identifier.urihttp://dx.doi.org/10.2319/072918-547.1
dc.identifier.urihttp://hdl.handle.net/11655/24323
dc.description.abstractObjectives: To determine the best bonding method of orthodontic attachment among monolithic zirconia, feldspathic porcelain, hybrid porcelain, and the impact of surface-conditioning methods using a three-dimensional optical profilometer after debonding. Materials and Methods: 56 feldspathic porcelain, 56 monolithic zirconia, and 56 hybrid porcelain samples were divided into four surface treatment subgroups: (1) hydrofluoric (HF) acid etch + silane, (2) Al2O3 sandblasting + silane, (3) silicoating (SiO2), and (4) diamond bur + silane. The specimens were tested to evaluate shear bond strength (SBS). Residual composite was removed after debonding. Three-dimensional white-light interferometry was used to obtain quantitative measurements on surface roughness. Results: The highest SBS value was found for the HF acid-etched feldspathic porcelain group. The average surface roughness values were significantly higher in all material groups in which diamond bur was applied, while roughening with Cojet provided average surface roughness values closer to the original material surface. Conclusions: Variations in structures of the materials and roughening techniques affected the SBS and surface roughness findings.
dc.language.isoen
dc.relation.isversionof10.2319/072918-547.1
dc.rightsAttribution 4.0 United States
dc.rightsinfo:eu-repo/semantics/openAccess
dc.rights.urihttps://creativecommons.org/licenses/by/4.0/
dc.subjectShear bond strength
dc.subjectSurface roughness
dc.subjectThree-dimensional optical profilometry
dc.titleBiomechanical Evaluation Between Orthodontic Attachment And Three Different Materials After Various Surface Treatments: A Three-Dimensional Optical Profilometry Analysis
dc.typeinfo:eu-repo/semantics/article
dc.typeinfo:eu-repo/semantics/publishedVersion
dc.relation.journalAngle Orthodontist
dc.contributor.departmentOrtodonti
dc.identifier.volume89
dc.identifier.issue5
dc.description.indexWoS
dc.description.indexScopus


Bu öğenin dosyaları:

Bu öğe aşağıdaki koleksiyon(lar)da görünmektedir.

Basit öğe kaydını göster

Attribution 4.0 United States
Aksi belirtilmediği sürece bu öğenin lisansı: Attribution 4.0 United States