Mechanical Properties And Water Sorption Of Two Experimental Glass Ionomer Cements With Hydroxyapatite Or Calcium Fluorapatite Formulation

Abstract

In this study the mechanical behavior and water sorption (Ws) of experimental glass-ionomer-cements (GICs) with hydroxyapatite (HA) or calcium fluorapatite (CFA) prototype formulations were examined. Specimens from two experimental and one commercially available GIC were prepared in three protocols; (1) according to the manufacturer's instructions, (2) with coating and (3) with heat application. The specimens were stored in distilled water or artificial saliva at 37 degrees C for 7- and 30-days. Flexural strength (FS), Vickers hardness (VHN) and Ws of GICs were evaluated. Experimental GICs showed higher FS values than commercial GIC (p<0.001). Higher FS and VHN values were observed when GICs were prepared according to manufacturer's recommendation. FS was affected only by GIC-type (eta(2)=0.027), whereas VHN was affected by GIC-type (eta(2)=0.331), treatment-protocols (eta(2)=0.067), storage-medium (eta(2)=0.100) and increased storage-duration (eta(2)=0.317). The tested parameters did not significantly influence the Ws of all tested GICs (p>0.05). The GICs with HA or CFA formulations might represent a promising approach due to their FS, VHN and Ws characteristics.